PLA

Plastic Raw Materials

Carson@jinanwanghai.com

Description

Properties	Test Method	Test Condition	Units	Typical Values
Physical
Melt Flow Rate	ASTM D-1238	220oC, 10Kg	g/10min	-
Specific Gravity	ASTM D-792	23oC	g/cm3	1.03
Ash	-	800oC,30min	%	-
Mechanical
Tensile Strength	ASTM D-638	50mm/min	MPa	46
Elongation at Break	ASTM D-638	50mm/min	%	14
Flexural Strength	ASTM D-790	2mm/min	MPa	62
Flexural Modulus	ASTM D-790	2mm/min	MPa	1800
Impact Strength, IZOD non-notched	ASTM D-256	23oC	KJ/m2	-
		-30oC	KJ/m2	-
Impact Strength, IZOD notched	ASTM D-256	23oC	KJ/m2	17
		-30oC	KJ/m2	-
Thermal
Heat Deflection Temp.	ASTM D-648	1.8Mpa	oC	93
		0.45Mpa	oC	98
Others
Mold Shrinkage	ASTM D-955	23oC	%	0.6-0.9
Flammability	UL94	1/16"		HB

Product transportation

We have cooperated with experienced shipping forwarders for many years, they arrange the shipment. No matter by express, by air or by sea, we will track the course of the goods all the way, to make sure goods arrive at you on time and in good condition.

Previous
ABS

Next
HIPS

GET A QUOTE

Whether you have any questions about our products, please feel free to contact us, we will reply as soon as possible.

PA

Specification: Polyamide (pa) type:Super Tough Grade,Reinforced Grade ,Flame-retardant Grade,Mineral Filled Grade PA Polyamide : polyamide pa 6 , pa 66 , pa plastic pipe Property : PA has the advantages of high mechanical strength, high softening point, good wear resistance, self-lubrication, cushioning, sound deadening, excellent oil and chemical corrosion resistance, and good electrical insulation. Because of these superior performances, PA composite has already replaced some metals being as structural materials. PA6 & PA66 Products Series and Specification : Product Series Type Specification Decription PA in the Electronic & Electrical Fields Ordinary Grade 5010 Good Flowa ...

POM

Polyoxymethylene is a linear polymer with no side chains, high density, and high crystallinity. According to the chemical structure in the molecular chain, it can be divided into two types: homopolyformaldehyde and acetal copolymer. The important difference between the two is that the homopolyformaldehyde has high density, crystallinity and melting point, but the thermal stability is poor, the processing temperature range is narrow (about 10 ° C), the acid-base stability is slightly lower, and the copolymerized formaldehyde density, crystallinity, The melting point and strength are low, but the thermal stability is good, it is not easy to decompose, the processing temperature range is wide (about 50 ° C), and the acid-base stability is good. It is an engineering plastic with excellent comprehensive performance. Has good physical, mechanical and chemical properties, especially with excellent friction resistance. Commonly known as Saigang or Steel, it is the third largest general plastic. Suitable for making wear-resistant parts, transmission parts, and parts such as chemicals and instruments. 1) Excellent mechanical strength; 2)High hardness strength; 3)High wear resist ...

Zinc oxide

CAS No. 1314-13-2 Purity 99.5% Place of Origin Fujian, China Classification Zinc Oxide Model Number Direct Zinc oxide Appearance White Powder Application Rubber, Varistor, paint,catalyst EINECS No. 215-222-5 Grade Standard Agriculture Grade, Electron Grade, Food Grade, Industrial Grade MF OZn Other Names Zinc oxide ...

PC

Polycarbonate (PC) is a molecular chain containing carbonate base polymer, according to the structure of the ester base can be divided into aliphatic, aromatic, aliphatic, aromatic, and other types.Because of aliphatic and mechanical properties of aliphatic and aromatic polycarbonate is low, which limits its application in the field of engineering plastics.There are only aromatic polycarbonate won the industrialized production.Due to the particularity of polycarbonate structure, has become the fastest growing in the five engineering plastics of general engineering plastics. 1.Properties PC is characterized by high transparency, high impact resistance, high hardness, high creep-resistance, excellent dimensional stability, good resistance to low-temperature and heat, flame retardance, ease to process, and excellent sound insulation Test Project Test Methods Unit ...

HDPE

Specifications Item Specification Density g/cm3 0.956 Melt Mass-Flow Rate(MFR) g/10min 0.04 Elongation at Break % min 500 Tensile Stress at Yield kg/cm2 230 Tensile Stress at Break kg/cm2 420 Tensile Strain at Break % 300 Flexural Modulus kg/cm2 1000 Durometer Hardness(D Scale, compression molded) 64 Power Ash % 0.01 Color: Half colorless Packing: 25kg pp bag, 17mt per 20FCL Application ： salt industry，aquaculture，agriculture，mining，petrochemical，environmental protection P.S: we also produce LDPE,LLDPE,ABS,PET,PS etc.,if you need,please contact our sales department . ...

We Provide Best Services
Agent

PLA

Carson@jinanwanghai.com

Previous
ABS

Next
HIPS

GET A QUOTE

Categories

Hot products

PA

POM

Zinc oxide

PC

HDPE

New Products

Follow Us

Useful Link

Products

Newsletter

Contact Us

Quality product supplier

Welcome to visit

PLA

ABS

HIPS

GET A QUOTE

Related products

Categories

Hot products

New Products

Useful Link

Products

Contact Us

Company profile

Quality product supplier

Welcome to visit

GET IN TOUCH!